Sintered Fire Magnesite Brick For Sale

1. High fire-resistant degree. 2. Good alkali tolerance. 3. High softening temperature under load.

Features:

Magnesia brick  is generally divided into sintered magnesia brick and chemical combination of magnesia brick, also known as unfired magnesia bricks. High purity and high baking temp magnesia brick,because of MgO grain contact directly, known as a direct combination of magnesia brick; the other kind is called electro-fused magnesia bricks.Sintered magnesia brick take magnesia brick as raw material, after ingredients, crushing, mixing, forming, and 1550 ~ 1600 °C temperatures firing. High purity products firing temperature is at 1750°C or more higher.

1. High fire-resistant degree.

2. Good alkali tolerance.

3. High softening temperature under load.

 

Applications:

No pouring magnesia brick produced by adding proper chemical bond, then mixing, forming and drying.

Mainly used in ceramic frit furnace, sodium silicate furnace, glass melting furnace regenerator, steeling furnace, bottom and wall of electric furnace, permanent lining of oxygen converter, non-ferrous metal

smelting furnace, high temperature tunnel kiln, sintered magnesia brick and cement kiln liner.

Sintered magnesia brick physiochemical index 

Item	Properties
	Magnesia brick			Magnesium aluminum bricks		Magnesium zirconium brick
	MZ-92	MZ-95	MZ-97	ML-80A	ML-8B	MZZ-1	MZZ-2
MgO	92	95	97	80	80	73	77
CaO	2.5	2.0	2.0	—	—	—	—
Al2O3	—	—	—	5-10	5-10	—	—
SiO2	4.0	2.0	1.0	—	—	—	—
ZrO2	—	—	—	—	—	12	12
Apparent porosity %	18	18	18	18	20	18	16
Cold Crushing strength MPa,	60	60	60	40	30	65	70
Softening temperature under load,°C,	1600	1650	1700	1600	1580	1600	1660
Permanent linear change,%,1650°CX 2 H	0-0.5	0-0.3	0-0.2	—	—	—	—
Bulk density,g/cm3	2.88	2.9	3.0	—	—	3.0	3.1
Application	sodium silicate furnace,ceramic frit furnace ,glass furnace, coking furnace, metallurgical furnace and other furnaces

 

Sintered Fire Magnesite Brick For Sale